Klüber WOLFRACOAT C High-temperature lubricating paste 60g tube

Klüber WOLFRACOAT C High-temperature lubricating paste 60g tube

$pics/Kluber/WOLFRACOAT C/kluber-wolfracoat-c-high-temperature-lubricating-paste-tube-60g-ol.jpg$

$pics/Kluber/WOLFRACOAT C/kluber-wolfracoat-c-high-temperature-lubricating-paste-tube-60g-ol.jpg$
$pics/Kluber/WOLFRACOAT C/kluber-wolfracoat-c-high-temperature-lubricating-paste-tube-60g-l.jpg$

€ 27.31 27.31 incl. VAT (22.95 excl. VAT), per piece *

Availability: Available

Packaging unit: 1 piece

Manufacturer: Klüber

Country of origin: BE/0017

Customs tariff number: 34039900

Weight per piece: 80 g

The product description does not help you?
No problem. Simply fill out the form and we will answer you as soon as possible.

Questions about the product

Title ×

Mr. Ms.

First name ×

Last name ×

e-mail ×

Telephone

Message ×

The fields marked with (×) are required.

Security (ANTI-SPAM)

zero - zero = ?

( Examples: two + three = 5, three - five = -2 )

Wolfracoat C is a grey high-temperature lubricating paste containing metal solid lubricant pigments (e.g. copper, graphite).
Wolfracoat C counteracts excessive friction, wear and seizing at lubricating points subject to high loads.
Wolfracoat C forms a thermally stable lubricating film. At temperatures above 200 °C, the solid lubricants remain in the friction points and protect against tribocorrosion and fretting of e.g. fits up to 1200 °C.
Temperature range: -30°C to +1200°C
Volume: 60g tube
Also available in: 400g cartridge, 1.2 kg can

Easier assembly and disassembly of power-locking connections
Reliable lubrication under mixed-friction and high-load conditions owing to ageing-resistant solid lubricants

Wolfracoat C is suitable for use as an assembly paste to lubricate power-locking connections and low-speed (plain) bearings subject to high temperatures.
Typical applications are in power plants, the steel industry, cement manufacture and similar industrial areas.

Apply the paste to clean surfaces or threads. It is important to obtain a uniform and coherent layer which is as thin as possible.
Any excess can removed with e.g. a leather cloth

Chemical composition, type of oil	synthetic hydrocarbon oil
Chemical composition, thickener	silicate
Chemical composition	solid lubricant
Lower service temperature	-30 °C / -22 °F
Upper service temperature	1200 °C / 2192 °F
Colour space	grey
Worked penetration, DIN ISO 2137, 25 °C, lower limit value	270 x 0.1 mm
Worked penetration, DIN ISO 2137, 25 °C, upper limit value	310 x 0.1 mm
Kinematic viscosity of the base oil, DIN 51562 pt. 01/ASTM D- 445/ASTM D 7042, 40 °C	approx. 110 mm²/s
Shear viscosity at 25 °C, shear rate 300 s-1, equipment: rotational viscometer, lower limit value	5 000 mPas