Bostik Simson ISR 70-08 AP SMP glazing adhesive for windscreens 290 ml

Bostik Simson ISR 70-08 AP SMP glazing adhesive for windscreens 290 ml

€ 20.17 20.17 incl. VAT (16.95 excl. VAT), per piece *

Availability: Available

Packaging unit: 1 piece

Manufacturer: BOSTIK

Country of origin: FR/0001

Customs tariff number: 32141010

Weight per piece: 450 g

The product description does not help you?
No problem. Simply fill out the form and we will answer you as soon as possible.

Questions about the product

Title ×

Mr. Ms.

First name ×

Last name ×

e-mail ×

Telephone

Message ×

The fields marked with (×) are required.

Security (ANTI-SPAM)

three + nine = ?

( Examples: two + three = 5, three - five = -2 )

Bostik Simson ISR 70-08 AP is specially designed for the rapid replacement of windscreens tt 23°C and 50% relative humidity

High quality Silyl Modified Polymer (SMP) based direct Glazing Adhesive
Especially developed for the rapid and efficient bonding of windscreens in the Auto Aftermarket as well as in OEM, Bus, Coach & Train building and other areas of the Transport market, especially where vehicles have to be released (or moved) shortly after installation
Color: black
Content: 290 ml cartridge
Also available as: 600 ml pack

Highlights

Bostik Simson ISR 70-08 AP combines the advantages of desired properties of structural sealants including polyurethanes
Simson ISR 70- 08 AP is not reliant on the primed system to provide a cross-linking covalent bond (less chances of applicator error)
Immediately after installation the product has a high Green Strength (a high internal strength), which results in a heavy paste with an extremely good slump resistance. Reaction starts with moisture and results in an irreversible vulcanized adhesive. The high green strength coupled to the high tack results in rapid bonding and makes the product very suitable for those applications where the vehicles have to be released (or moved) shortly after installation
Bostik Simson ISR 70-08 AP adheres well without black glass primer on glass and no UV resistant primer is needed when the glass adhesive interface is adequately UV-protected by a ceramic coating
Solvent-isocyanate- and PVC free
Excellent UV resistance and ageing properties
Excellent temperature resistance, permanent elastic within temperatures from –40°C till +120°C
No odour
Paintable
Very low electrical conductivity
Suitable for use with window aerials
Prevents contact corrosion on aluminium substrates
Non staining – less than 1% carbon black content
Possible reduced or no clamping required

Technical specifications

Colour	Black
Basic Material	Silyl Modified Polymer (SMP)
Specific Gravity	Approx. 1.5
Curing Method	Moisture
Skin Forming Time	approx. 15 min (20°C/50% R.H.)
Open Time	<15 min. (20°C/50% R.H.)
Tensile Stress at Break	approx. 2.9 MPa (DIN 53504/ISO37)
Elongation at Break	approx. 250% (DIN 53504/ISO37)
Shear Stress	approx. 2.4 MPa (DIN 53283/ ASTM D1002)
Isocyanate Percentage	0%
Temperature Resistance	-40°C to+120°C
Temperature Resistance	+180°C (max ½ hr.)
Curing Speed after 24 hrs	approx. 3 mm (20°C/50% R.H.)
Shore A Hardness	approx. 60 (DIN 53505)
Volume Change	<3% (DIN 52451)
Electrical Volume Resistivity	>1011 cm (DIN 53428)
Tensile Stress (100%)	Approx. 2.3 MPa (DIN 53504/ISO37)